View MCH438FN476ZP_1277713.PDF datasheet online --- IC-ON-LINE

Datasheet File OCR Text:

MCH43
Ceramic capacitors
Multi-layer ceramic chip capacitors
MCH43 (4532 (1812) size, chip capacitor)
Features 1) High capacitance 2) Achieved high capacitance by thin and multi layer technology 3) Lead-free plating terminal 4) No polarity
Quick Reference The design and specifications are subject to change without prior notice. Please check the most recent technical specifications prior to placing orders or using the product. For more detail information regarding packaging style code, please check product designation.
Thermal compensation
Part No. Size code Temperature characteristics (ppm/C) code Operating temp. range (C) Rated voltage (V) Capacitance (pF) Capacitance tolerance Thickness (mm)
MCH43
4532 (1812)
AN
030 (CG) (C0G)
-55 to +125
50
150,000 (E6 Series) 220,000 (E6 Series)
J(5%)
2.5 0.3 3.2 0.3
High dielectric constant
Part No. Size code code Temperature characteristics
Operating temp. range (C)
Rated voltage (V)
50
Capacitance (pF)
Capacitance tolerance
Thickness (mm)
10% (B)
-25 to +85 25 50 -55 to +125 25 16
15% (R) (X7R)
CN
MCH43
4532 (1812)
15% (X5R)
-55 to +85 10 6.3 50 25 16 10 50 25 16 10
+30% , -80% (F)
-25 to +85
FN
+22% , -82% (Y5V)
-30 to +85
2,200,000 (E6 Series) 3,300,000 (E6 Series) 4,700,000 (E6 Series) 6,800,000 (E6 Series) 2,200,000 (E6 Series) 3,300,000 (E6 Series) 4,700,000 (E6 Series) 6,800,000 (E6 Series) 10,000,000 (E6 Series) 15,000,000 (E6 Series) 22,000,000 (E6 Series) 33,000,000 (E6 Series) 47,000,000 (E6 Series) 68,000,000 to 100,000,000 (E6 Series) 10,000,000 (E3 Series) 22,000,000 (E3 Series) 47,000,000 (E3 Series) 100,000,000 (E3 Series) 10,000,000 (E3 Series) 22,000,000 (E3 Series) 47,000,000 (E3 Series) 100,000,000 (E3 Series)
K(10%)
1.6 0.2 2.0 0.2 1.6 0.2 2.0 0.2 1.6 0.2 2.0 0.2 1.6 0.2 2.0 0.2 2.5 0.3 2.3 0.2 2.5 0.3 2.3 0.2 2.8 0.3 2.0 0.2 2.5 0.3
M(20%)
Z(+80% , -20%)
2.0 0.2 2.5 0.3
1/10
MCH43
Ceramic capacitors
External dimensions (Unit : mm)
Product thickness(mm) 1.60.2 2.00.2 2.30.2 2.50.3 2.80.3 3.20.3
T
0.2Min.
T
4.50.4
3.20.4
Product designation
Code Product thickness P P P P P P 1.6mm 2.0mm 2.3mm 2.5mm 2.8mm 3.2mm Packing specification Plustic tape (width 12mm, pitch 8mm) Plustic tape (width 12mm, pitch 8mm) Plustic tape (width 12mm, pitch 8mm) Plustic tape (width 12mm, pitch 8mm) Plustic tape (width 12mm, pitch 8mm) Plustic tape (width 12mm, pitch 8mm) Reel 180mm (7in.) 180mm (7in.) 180mm (7in.) 180mm (7in.) 180mm (7in.) 180mm (7in.) Basic ordering unit (pcs.) 1,000 1,000 500 500 500 500
Reel (180mm) : compatible with EIAJ ET-7200A
Part No.
Packing Style
MCH
Rated voltage
Code Voltage 8 4 3 2 5 6.3V 10V 16V 25V 50V
43
3
FN
476
Z
P
Nominal capacitance 3-digit designation according to IEC Capacitance tolerance Tolerance Code J K M Z
Temperature characteristic code : Refer to quick reference table.
5% (11pF or more) 10% 20%
+80%, -20%
2/10
MCH43
Ceramic capacitors
*Performance and test method
No.
1
Items Appearance and dimensions
Performance
Test Method (As per JIS C 5101-1, JIS C 5101-10)
No marked defects shall be allowed As per 4.4 of JIS C 5101-1. As per 4.5 of JIS C 5101-10 for appearance. Dimensions shall be as specified the Using a Magnifier. clause 4.
No dielectrical breakdown or other damage shall be allowed.
2
Withstanding voltage
As per 4.6 of JIS C 5101-1. As per 4.6.4 of JIS C 5101-10 Voltage shall be applied as per Table1. Table 1 CharacVoltage teristic 300% Rated voltage AN CN 250% Rated voltage FN
Voltage shall be applied for 1 to 5s with 50mA charging and discharging current.
3
Insulation resistance
Not less than 10000M or 500M F, whichever is less. (For products with rated voltage less than 16V, it is not less than 10000M or 100M F, whichever is less.)
As per 4.5 of JIS C 5101-1. As per 4.6.3 of JIS C 5101-10 Measurements shall be made after 60+/-5s period of the rated voltage applied. As per 4.7 of JIS C 5101-1. As per 4.6.1 of JIS C 5101-10 Measurements shall be made under the conditions specified in Table 2.
Characteristic AN
CN FN
4
Capacitance
Capacitance shall be within specified tolerance range.
Table 2 Frequency Voltage
1+/-0.1kHz 0.5 to 5Vrms. < 10F > 10F - 1+/-0.1KHz 120+/-24Hz 1+/-0.2Vrms. 0.5+/-0.2Vrms.
5 Dielectric loss tangent
AN
tan < 0.1% -
As per 4.8 of JIS C 5101-1. As per 4.6.2 of JIS C 5101-10 Measurements shall be made under the conditions specified in Table 2.
CN
Rated voltage=16, 10V tan < 7.5% - Rated voltage=6.3V tan < 10.0% -
FN
Rated voltage=16V tan < 10.0% - Rated voltage=10V tan < 12.5% -
3/10
MCH43
Ceramic capacitors
No.
Items
Performance
Test Method (As per JIS C 5101-1, JIS C 5101-10) As per 4.24 of JIS C 5101-1. As per 4.7 of JIS C 5101-10 Temperature coefficient shall be calculated at 20C and 85C. As per 4.24 of JIS C 5101-1. As per 4.7 of JIS C 5101-10 If required, measurements shall be made at a given temperature.
6 Temperature characteristic
AN
0+/-30ppm / C (-55C to +125C) +/-10% (-25C to +85C) +/-15% (-55C to +85C)
CN
B
X5R
FN
+30%, -80% (-25C to +85C) +22%, -82% (-30C to +85C) As per 4.15.2 of JIS C 5101-1. As per 4.11 of JIS C 5101-10 The solder specified in JIS Z 3282 H63A shall be used. Ans the flux containing 25% rosin and ethanol solution shall be used. The specimens shall be immersed into the solder at 235+/-5C for 2+/-0.5s So that both end terminations are completely under solder. As per 4.14 of JIS C 5101-1. As per 4.10 of JIS C 5101-10 The solder specified in JIS Z 3282. H63A shall be used. The specimens shall be immersed into the solder at 260+/-5C for 5+/-0.5s so that both end terminations are completely under the solder. Pre-heating at 150+/-10C for 1 to 2min Initial measurements prior to test shall be performed after the thermal Pre-conditioning specified in Remarks (1). Final measurements shall be made after the specimens have been left at room temperature as per Table3. Table3 Characteristic AN CN, FN Time 24+/-2 h 48+/-4 h
7 Solderability
More than 3/4 of each end termination shall be covered with new solder.
8 Resistance to solderin heat
Appearance Without mechanical damage.
Change rate from initial value
AN
Within +/-2.5% Within +/-7.5% Within +/-20%
CN
FN
Dielectric loss tangent Insulation resistance
Within specified initial value.
Within specified initial value.
Withstanding No defects shall be allowed. voltage
9 End termination adherence
Without peeling or sign of peeling shall be allowed on the end terminations.
As per 4.13 of JIS C 5101-1. As per 4.8 ofJIS C 5101-10 A 5N weight for 10+/-1s shall be applied to the soldered specimens as shown by the arrow mark in the below sketch.
Applied pressure
Substrate
Capacitor
4/10
MCH43
Ceramic capacitors
No.
10 Bending strength
Items
Performance
Test Method (As per JIS C 5101-1, JIS C 5101-10) As per 4.35 of JIS C 5101-1. As per 4.9 of JIS C 5101-10 Glass epoxy board with soldered specimens shall be bent till 1mm by 1.0mm/s. As per 4.17 of JIS C 5101-1. The specimens shall be soldered on the specified test jig. Initial measurements shall be made after the thermal pre-conditioning specified in Remarks(1). Final measurements shall be made after the specimens have been left at room temperature as per Table3. [Condition] Directions : 2h each X, Y and Z directions Total : 6h Frequency range : 10 to 55 to 10Hz(1min) Applitude : 1.5mm (shall not exceed acceleration196m/s2) Table3 Characteristic AN CN, FN Time 24+/-2 h 48+/-4 h
Appearance
Without mechanical damage.
11 Vibration
Appearance Change rate from initial value
Without mechanical damage.
Capacitance shall be within specified tolerance range. Within +/-7.5% Within +/-20%
AN
CN
FN
Dielectric loss tangent
Within specified initial value.
12 Temperature Appearance Without mechanical damage. cycling Change AN Within +/-2.5% rate from initial value
Rated voltage C N 25V,16V,10V Within +/-7.5% Rated voltage Within +/-10% 6.3V FN
Within +/-20%
As per 4.16 of JIS C 5101-1 As per 4.12 of JIS C 5101-10 The specimens shall be soldered on the test jig shown in Remarks. Temperature cycle : 100cycles Initial measurements prior to test shall be performed after the thermal per-conditioning specified in Remarks (1). Final measurements shall be made after the specimens have been left at room temperature as per Table3. Test condition Step Temp. (C) Min operating temp. Room temp. Max operating temp. Room temp. Table3 Characteristic AN CN, FN Time 24+/-2 h 48+/-4 h Time (min) 30+/-3 <3 - 30+/-3 < -3 1 2 3 4
Dielectric loss tangent Insulation resistance
Within specified initial value. Within specified initial value.
Withstanding No defects shall be allowed. voltage
5/10
MCH43
Ceramic capacitors
No.
13 Humidity (Steady)
Items
Performance
Test Method (As per JIS C 5101-1, JIS C 5101-10)
Appearance Without mechanical damage. Change rate from initial value
Dielectric tangent
As per 4.22 of JIS C 5101-1 JIS C 5101-10 Within +/-5.0% AN Test temperature : 60+/-2C Relative humidity : 90 to 95% Rated voltage : 500 +24/-0 h 25V,16V,10V Within +/-12.5% Test time CN Initial measurements prior to test shall Rated voltage Within +/-25.0% 6.3V be made after the voltage pre-conditioning specified in Within +/-30% FN Remarks (2). Final measurements have been left at tan < 0.3% AN - room temperature as per Table3.
CN
Less than 200% of initial spec. Less than 150% of initial spec.
Characteristic AN CN, FN
Table3
Time
FN
Insulation resistance
Not less than 1000M or 50M F, whichever is less. (For products with rated voltage less than 16V, it is not less than 1000M or 10M F, whichever is less.)
24+/-2 h 48+/-4 h
14 Humidity life test
Appearance Without mechanical damage. Change rate from initial value
Dielectric loss tangent
Insulation resistance
As per 4.22 of JIS C 5101-1 As per 4.14 of JIS C 5101-10 Within +/-7.5% AN Test temperature : 60+/-2C Relative humidity : 90 to 95% Rated voltage 25V,16V,10V Within +/-12.5% Voltage : Rated voltage CN Test time : 500 +24/-0 h Rated voltage Within +/-25.0% Initial measurements prior to test shall 6.3V be made after the voltage FN Within +/-30% pre-conditioning specified in Remarks (2). AN tan < 0.3% - Final measurements shall be made after the specimens have been left at room Less than 200% of temperature as per Table3. CN initial spec. Table3 Less than 150% of FN initial spec. CharacTime teristic Not less than 500M or AN 24+/-2 h 25M F, whichever is less. (For products with rated voltage less CN, FN 48+/-4 h than 16V, it is not less than 500m or 5M F, whichever is less.)
6/10
MCH43
Ceramic capacitors
No. 15 Heat life test
Items
Performance
Test Method (As per JIS C 5101-1, JIS C 5101-10)
Appearance Without mechanical damage. Change rate from initial value
CN AN
Within +/-3.0%
As per 4.23 of JIS C 5101-1. As per 4.15 of JIS C 5101-10
Test Voltage temperature(C) AN 125 200% Rated voltage 200% Rated voltage 200% Rated voltage Test time (h) 1000 +48/-0 1000 +48/-0 1000 +48/-0
Rated voltage 25V,16V,10V Within +/-15% Rated voltage Within +/-25% 6.3V FN
Within +/-30%
CN
Dielectric loss tangent
AN
tan < 0.5% -
Less than 200% of initial spec. Less than 150% of initial spec.
85 (B X5R) 85
FN
CN
FN
Insulation resistance
Not less than 1000M or 50M F, whichever is less. (For products with rated voltage less than 16V, it is not less than 1000m or 10M F, whichever is less.)
Initial measurements prior to test shall be made after the voltage pre-conditioning specified in Remarks (2). Final measurements shall be made after the specimens have been left at room temperature Table3 Characteristic AN CN, FN Time 24+/-2 h 48+/-4 h
[Remarks] Pre-conditioning If specified in test method of as per 3(Performance and test merhod), capacitors of CN, FN characteristics shall be pre-conditionded as follows. (1) Thermal pre-conditioning Prior to initial measurements, specimens shall be conditioned at a temperature of 150 0/-10C for a period of 1hr., and shall be allowed to stabilize at room temperature for 48+/-4h (2) Voltage pre-conditioning Prior to initial measurements, voltage specified as a test condition shall be applied to specimens for a period of 1hr., and the specimens shall be allowed to stabilize at room temperature for 48+/-4h

Soldering
Glass epoxy substrate
7/10
MCH43
Ceramic capacitors
Packaging specifications
Taping dimensions
J E
t
Reel dimensions
A
D
14.0 +1.5 -
B
C
13.0 + 0.2 -
60.0+1.0 -0
F
G
H
Pulling direction
t1
P : Plastic tape
Symbol
C
D
E
F
G
H
J
t
t1 6.5 MAX.
Label pasting
Plastic
0.6 12.0 5.5 1.75 8.0 2.0 4.0 1.5 Dimensions +/ -0.3 +/ -0.05 +/ -0.1 +/ -0.1 +/ -0.05 +/ -0.1 +0.1/ -0 MAX.
Symbol Style
MCH43
(Unit : mm)
A B
As per EIAJ ET-7200A
(Unit : mm)
3.6
4.9
(Unit : mm)
(1) The quantity for one reel is as bellows.
Kind of reel
180 reel
Series
MCH43
Plastic tape Quantity
500 pcs.
Symbol
P
(2) When the tape is pulled out towards the operator with the cover tape facing upward, the feeding holes shall be found on the right portion of the tape. (3) Specification of beginning and ending of the tape are as follows.
Ending(reel's center) Beginning(reel's round) : Approx. Over 160mm (no chips) : Approx. Over 160mm (no chips) : Approx. 240mm (cover tape only)
(4) No juncture of tape shall be allowed. (5) The share strength of tape shall be more than 5N at the break down strength. (6) The peel strength of the cover tape shall be 0.1 to 0.7(N) when the cover tape are peeled 0 to 15 degree from the surface. (7) The number of missing components shall not exceed 0.1% of the total number of components (marked number) or one whichever is the larger, and no consecutive missing exceeding two is allowed. (8) The reels made from resin shall be used, as per EIAJ ET-7200A.
Marking No marking shall be performed on the chip. Trademark, parts number, quantity, lot No. , and country of origin shall be labeled on each reel. Numbering system for LOT No.
Example
03 (1)
01 (2)
A0001 (3)
F (4)
(1) The end of the Christian Era < two digits> of production finish. (2) Week in completing part of production finish. (3) Manufacture continuity number. (4) The symbol of manufacturing plant.
+0 180 -1.5
8/10
MCH43
Ceramic capacitors
Label expression The Figure below is label expression < Label Example > Part Number : MCH435AN104JP
Part Number Division cord Quantity Lot No. The Country of origin Inspector QR code Trademark
Packing method 1) 180mm Reel
EIAJ cole
2
B'
C'
(reel) Label
A'
[width of 9mm : 5reel]
1
A
Packing slip
(interior box of R-26)
B
C
(R-26)
9/10
MCH43
Ceramic capacitors
< Packaging unit >
Symbol Quantity of reel in interior box Quantity of reel in box of R-26 K 3 12 Dimensions R-26 A (A') B (B') C (C') 195 255 190 Packaging interior box ofR-26 185 60 185 (Unit : mm)
< Appearance >
Carton
< Accumulation >
You must do accumulation by ten boxes
< Packaging slip >
1. 2. 3. 4. 5. Customer Parts number Quantity Box quantity Trade mark
10/10
Appendix
Notes
No technical content pages of this document may be reproduced in any form or transmitted by any means without prior permission of ROHM CO.,LTD. The contents described herein are subject to change without notice. The specifications for the product described in this document are for reference only. Upon actual use, therefore, please request that specifications to be separately delivered. Application circuit diagrams and circuit constants contained herein are shown as examples of standard use and operation. Please pay careful attention to the peripheral conditions when designing circuits and deciding upon circuit constants in the set. Any data, including, but not limited to application circuit diagrams information, described herein are intended only as illustrations of such devices and not as the specifications for such devices. ROHM CO.,LTD. disclaims any warranty that any use of such devices shall be free from infringement of any third party's intellectual property rights or other proprietary rights, and further, assumes no liability of whatsoever nature in the event of any such infringement, or arising from or connected with or related to the use of such devices. Upon the sale of any such devices, other than for buyer's right to use such devices itself, resell or otherwise dispose of the same, no express or implied right or license to practice or commercially exploit any intellectual property rights or other proprietary rights owned or controlled by ROHM CO., LTD. is granted to any such buyer. Products listed in this document are no antiradiation design.
The products listed in this document are designed to be used with ordinary electronic equipment or devices (such as audio visual equipment, office-automation equipment, communications devices, electrical appliances and electronic toys). Should you intend to use these products with equipment or devices which require an extremely high level of reliability and the malfunction of with would directly endanger human life (such as medical instruments, transportation equipment, aerospace machinery, nuclear-reactor controllers, fuel controllers and other safety devices), please be sure to consult with our sales representative in advance. About Export Control Order in Japan Products described herein are the objects of controlled goods in Annex 1 (Item 16) of Export Trade Control Order in Japan. In case of export from Japan, please confirm if it applies to "objective" criteria or an "informed" (by MITI clause) on the basis of "catch all controls for Non-Proliferation of Weapons of Mass Destruction.
Appendix1-Rev1.1

▲Up To Search▲

Price & Availability of MCH438FN476ZP

	To Download MCH438FN476ZP Datasheet File
If you can't view the Datasheet, Please click here to try to view without PDF Reader .